What is 6063 T6 aluminum used for?
Aluminium alloy 6063 is a medium strength alloy commonly referred to as an architectural alloy. It is normally used in intricate extrusions. It has a good surface finish, high corrosion resistance, is readily suited to welding and can be easily anodised.
What is the difference between 6061 T6 and 6063 T6?
For example, in comparing aluminum alloy 6061 t6 vs 6063 t6, we know that 6061 t6 has an ultimate tensile strength of at least 42,000 psi and yield strength of at least 35,000 psi. This is compared to the 6063 t6 ultimate tensile strength of at least 28,000 psi and yield strength of 23,000 psi.
How strong is 6063 T6 aluminum?
6063-T6. T6 temper 6063 has an ultimate tensile strength of at least 190 MPa (28,000 psi) and yield strength of at least 160 MPa (23,000 psi). In thicknesses of 3.15 millimetres (0.124 in) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%.
What is the difference between 6063 T5 and 6063 T6?
It has very good corrosion resistance and almost no anti-rust treatment T5 or T6 means heat-treatment level, which is related to the hardness. For the same product, T6 is better than T5. For most products, T5 is enough, and T6 is better. For hollow products, it would have a risk of out-of-shape when you insist on T6.
Is 6063 T6 aluminum bendable?
Combining its formability, high strength-to-weight ratio and great corrosion resistance, 6063 aluminum is the preferred choice for bending aluminum into a variety of architectural and industrial applications that require detailed geometries.
What is the difference between aluminum 6061 and 6063?
What Are 6061 & 6063 Aluminum Alloyed With? 6061 and 6063 both share the same alloying elements. 6061 aluminum can have up to double the iron and typically has substantially more silicon, copper, and chromium than 6063 aluminum. In general, you’ll find that 6061 has more of each alloying element than 6063.
What is the hardness of 6063 aluminum?
Brinell 73 73
Aluminum 6063-T6
Physical Properties | Metric | English |
---|---|---|
Hardness, Brinell | 73 | 73 |
Hardness, Knoop | 96 | 96 |
Hardness, Vickers | 83 | 83 |
Ultimate Tensile Strength | 241 MPa | 35000 psi |
What are the properties of 6063 T6 aluminum alloy?
Aluminum alloy 6063 t6 has excellent properties such as good strength, anti-corrosion and wear-resistance, and high temperature resistance. It is mostly used in construction and industrial fields.
What is the tensile strength of 6063 steel?
T6 temper 6063 grade has an ultimate tensile strength of at least 190MPa (28,000psi) and a yield strength of at least 160MPa (23,000psi). At a thinner thickness, such as 3.15 mm (0.124 inch) or less, its elongation is 8% or higher; at a thicker thickness, it can reach an elongation of 10%. Can aluminium alloy 6063 be welded?
What is the 6063-t6 “temper”?
Each “temper” has its own distinct qualities, but this article will only focus on the 6063-T6 temper for simplification. The tensile yield strength is a measure of how much tensile (pulling) stress a piece of 6063 aluminum can take before plastically (or permanently) deforming.
Is 6063 a good material for extrusion?
Physical Properties of 6063 Aluminum 6063 aluminum alloy is heat treatable, weld-able, good at resisting corrosion and easily formed. It is a top choice for extrusion because of its properties, as it is easily pushed through a die into many fixed-cross sectional shapes.